Fabrication of ZnO nanoparticles confined in the channels of mesoporous carbon

Ulka Suryavanshi, Toru Iijima, Akari Hayashi, Yasuhiko Hayashi, Masaki Tanemura

Research output: Contribution to journalArticlepeer-review

34 Citations (Scopus)


ZnO nanoparticles have been incorporated inside the pore system of mesoporous carbon (MC) which has been synthesized by polymerization of resorcinol and formaldehyde via soft templating approach. 5-20% of ZnO, with an interval of 5, have been incorporated almost exclusively within the mesopores by simple wet impregnation, drying and calcination procedures. The pristine MC shows high surface area (600m 2/g) with large pore diameter around 7nm. After impregnation of ZnO in mesopores, the pore diameter has been decreased from 7 to 6.24nm which may relate to shrinkage of the framework or deposition of ZnO particles on the inner wall of the pores. With the increase in the ZnO percentage, the specific surface area and pore volume decreased linearly confirming the incorporation of nanoparticles inside the mesopores. TGA confirms ZnO confined in the pores of MC which also prevents the collapsing of mesoporous carbon framework upto 325°C. Interestingly, the graphitic nature of MC remains same even after impregnation of ZnO nanoparticles inside the pores. However, we strongly believe that this novel composite of ZnO and MC may play significant role in the application like oxygen reduction reactions, photocatalysis, photovoltaics, optoelectronics, catalysis and many more.

Original languageEnglish
Pages (from-to)388-393
Number of pages6
JournalChemical Engineering Journal
Publication statusPublished - Jan 1 2012
Externally publishedYes


  • Carbon
  • Mesoporous
  • Soft template
  • ZnO

ASJC Scopus subject areas

  • General Chemistry
  • Environmental Chemistry
  • General Chemical Engineering
  • Industrial and Manufacturing Engineering


Dive into the research topics of 'Fabrication of ZnO nanoparticles confined in the channels of mesoporous carbon'. Together they form a unique fingerprint.

Cite this