TY - GEN
T1 - Formation of nano- and micrometer-scale hydroxyapatite rod array structure on ca-containing glass
AU - Hayakawa, Satoshi
AU - Kazama, Hiroshi
AU - Tsuru, Kanji
AU - Osaka, Akiyoshi
AU - Fujii, Eiji
AU - Kawabata, Koji
PY - 2008/12/1
Y1 - 2008/12/1
N2 - Nano- and micrometer-scale rod array structure of HAp having preferred orientation was successfully prepared by soaking calcium-containing borosilicate glass substrates in Na2HPO4 aqueous solution at 80°C for 7 days. Nano-scale HAp rods grew up perpendicularly to the glass surface, and the crystallites were arranged on the glass entire surface uniformly with preferred orientation to the c-axis.
AB - Nano- and micrometer-scale rod array structure of HAp having preferred orientation was successfully prepared by soaking calcium-containing borosilicate glass substrates in Na2HPO4 aqueous solution at 80°C for 7 days. Nano-scale HAp rods grew up perpendicularly to the glass surface, and the crystallites were arranged on the glass entire surface uniformly with preferred orientation to the c-axis.
UR - http://www.scopus.com/inward/record.url?scp=84869063021&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84869063021&partnerID=8YFLogxK
M3 - Conference contribution
AN - SCOPUS:84869063021
SN - 9781615670802
T3 - 8th World Biomaterials Congress 2008
BT - 8th World Biomaterials Congress 2008
T2 - 8th World Biomaterials Congress 2008, WBC 2008
Y2 - 28 May 2008 through 1 June 2008
ER -