Three-dimensional observation and analysis of remineralization in dentinal caries lesions

Kumiko Yoshihara, Noriyuki Nagaoka, Akiko Nakamura, Toru Hara, Satoshi Hayakawa, Yasuhiro Yoshida, Bart Van Meerbeek

Research output: Contribution to journalArticlepeer-review

16 Citations (Scopus)


The remineralization mechanism in dental caries lesions is not completely understood. This study reports on ultrastructural and chemical changes observed within arrested caries lesions. Carious human teeth were observed using scanning electron microscopy (SEM) and focused-ion-beam (FIB)-SEM. The crystals detected in the caries lesions were characterized by transmission electron microscopy (TEM), along with chemical element mapping using energy-dispersive spectroscopy (EDS)-STEM. FIB-SEM 3D reconstructions revealed a severely damaged dentin surface abundantly covered by bacteria. Although the dentin tubules were clogged up to a depth of 100 μm, bacterial invasion into dentin tubules was not observed. TEM crystal analysis and EDS-STEM revealed the presence of Ca and P, as well as of Mg within the HAp crystals deposited inside the dentin tubules. It was concluded that extensive remineralization with deposition of Mg-HAp crystals had occurred in dentin tubules of caries-arrested dentin. Understanding the natural remineralization process is thought to be helpful for developing clinical biomimetic remineralization protocols.

Original languageEnglish
Article number4387
JournalScientific reports
Issue number1
Publication statusPublished - Dec 1 2020

ASJC Scopus subject areas

  • General


Dive into the research topics of 'Three-dimensional observation and analysis of remineralization in dentinal caries lesions'. Together they form a unique fingerprint.

Cite this