Viscosity change and structural transition of Molten Fe at 5 GPa

The in situ viscosity measurements of the pure molten Fe under high pressures were made by falling sphere X-ray radiography method. Viscosity coefficients at about 2000 K were 15-24 mPa s at 2.7-5.0 GPa, and 4-9 mPa s at 5.0-7.0 GPa. Drastic decrease was found at around 5 GPa, at which stable solid phase below the melting temperatures change from delta (bcc) to gamma (fcc) phases. The observation indicates the possibility that the structural change in the molten Fe occurs in a narrow pressure interval (1 GPa) at the similar condition with the phase transformation in the solid.