Chemical and Mechanical Stability of the Ba-added High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System

Jun Takada; Kosei Fujisaka; Katsunori Hosotani; Toshio Egi; Yoshihiro Kusano; Tokuro Nanba; Yasunori Ikeda; Mikio Takano

doi:10.2497/jjspm.40.204

Chemical and Mechanical Stability of the Ba-added High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System

Jun Takada
, Kosei Fujisaka
, Katsunori Hosotani
, Toshio Egi
, Yoshihiro Kusano
, Tokuro Nanba
, Yasunori Ikeda
, Mikio Takano

研究成果 › 査読

抄録

Chemical and mechanical stability of the Ba-added high-Tc phase has been studied using XRD and DTA for samples of Bi_0.9Pb_0.2Sr_1.0Ba_xCa_1.0Cu_1.6Oz with x=0 and 0.05. Some impurities were observed in all samples after the heat treatment at 300∼820°C. BaPb_0.75Bi_0.25O₃ was also formed in the Ba-added samples heated at 700∼800°C. These impurities were thought to be formed from the amorphous phase which was produced by mechanical grinding of the high-Tc phase. The impurities disappeared and an almost monophasic sample of the high-Tc phase was obtained by heating at 850°C. The lattice parameter c of the Ba-added high-Tc phase was longer than that of the Ba-free one above 800°C. The parameter c of the Ba-added sample heated at 850°C increased with an increase of heating time and was saturated over 48h. The increase of c was due to the Ba dissolution in the high-Tc phase.

本文言語	English
ページ（範囲）	204-207
ページ数	4
ジャーナル	Journal of the Japan Society of Powder and Powder Metallurgy
巻	40
号	2
DOI	https://doi.org/10.2497/jjspm.40.204
出版ステータス	Published - 1993

ASJC Scopus subject areas

機械工学
産業および生産工学
金属および合金
材料化学

文献へのアクセス

10.2497/jjspm.40.204

他のファイルとリンク

引用スタイル

@article{6dd4b45ce5874295bcc819d1c59b030c,

title = "Chemical and Mechanical Stability of the Ba-added High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System",

abstract = "Chemical and mechanical stability of the Ba-added high-Tc phase has been studied using XRD and DTA for samples of Bi0.9Pb0.2Sr1.0BaxCa1.0Cu1.6Oz with x=0 and 0.05. Some impurities were observed in all samples after the heat treatment at 300∼820°C. BaPb0.75Bi0.25O3 was also formed in the Ba-added samples heated at 700∼800°C. These impurities were thought to be formed from the amorphous phase which was produced by mechanical grinding of the high-Tc phase. The impurities disappeared and an almost monophasic sample of the high-Tc phase was obtained by heating at 850°C. The lattice parameter c of the Ba-added high-Tc phase was longer than that of the Ba-free one above 800°C. The parameter c of the Ba-added sample heated at 850°C increased with an increase of heating time and was saturated over 48h. The increase of c was due to the Ba dissolution in the high-Tc phase.",

author = "Jun Takada and Kosei Fujisaka and Katsunori Hosotani and Toshio Egi and Yoshihiro Kusano and Tokuro Nanba and Yasunori Ikeda and Mikio Takano",

year = "1993",

doi = "10.2497/jjspm.40.204",

language = "English",

volume = "40",

pages = "204--207",

journal = "Journal of the Japan Society of Powder and Powder Metallurgy",

issn = "0532-8799",

publisher = "Journal of the Japan Society of Powder and Powder Metallurgy",

number = "2",

}

TY - JOUR

T1 - Chemical and Mechanical Stability of the Ba-added High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System

AU - Takada, Jun

AU - Fujisaka, Kosei

AU - Hosotani, Katsunori

AU - Egi, Toshio

AU - Kusano, Yoshihiro

AU - Nanba, Tokuro

AU - Ikeda, Yasunori

AU - Takano, Mikio

PY - 1993

Y1 - 1993

N2 - Chemical and mechanical stability of the Ba-added high-Tc phase has been studied using XRD and DTA for samples of Bi0.9Pb0.2Sr1.0BaxCa1.0Cu1.6Oz with x=0 and 0.05. Some impurities were observed in all samples after the heat treatment at 300∼820°C. BaPb0.75Bi0.25O3 was also formed in the Ba-added samples heated at 700∼800°C. These impurities were thought to be formed from the amorphous phase which was produced by mechanical grinding of the high-Tc phase. The impurities disappeared and an almost monophasic sample of the high-Tc phase was obtained by heating at 850°C. The lattice parameter c of the Ba-added high-Tc phase was longer than that of the Ba-free one above 800°C. The parameter c of the Ba-added sample heated at 850°C increased with an increase of heating time and was saturated over 48h. The increase of c was due to the Ba dissolution in the high-Tc phase.

AB - Chemical and mechanical stability of the Ba-added high-Tc phase has been studied using XRD and DTA for samples of Bi0.9Pb0.2Sr1.0BaxCa1.0Cu1.6Oz with x=0 and 0.05. Some impurities were observed in all samples after the heat treatment at 300∼820°C. BaPb0.75Bi0.25O3 was also formed in the Ba-added samples heated at 700∼800°C. These impurities were thought to be formed from the amorphous phase which was produced by mechanical grinding of the high-Tc phase. The impurities disappeared and an almost monophasic sample of the high-Tc phase was obtained by heating at 850°C. The lattice parameter c of the Ba-added high-Tc phase was longer than that of the Ba-free one above 800°C. The parameter c of the Ba-added sample heated at 850°C increased with an increase of heating time and was saturated over 48h. The increase of c was due to the Ba dissolution in the high-Tc phase.

UR - https://www.scopus.com/pages/publications/0027540871

UR - https://www.scopus.com/pages/publications/0027540871#tab=citedBy

U2 - 10.2497/jjspm.40.204

DO - 10.2497/jjspm.40.204

M3 - Article

AN - SCOPUS:0027540871

SN - 0532-8799

VL - 40

SP - 204

EP - 207

JO - Journal of the Japan Society of Powder and Powder Metallurgy

JF - Journal of the Japan Society of Powder and Powder Metallurgy

IS - 2

ER -

Chemical and Mechanical Stability of the Ba-added High-Tc Phase in the Bi-Pb-Sr-Ca-Cu-O System

抄録

ASJC Scopus subject areas

文献へのアクセス

他のファイルとリンク

フィンガープリント

引用スタイル